High Temperature Coarsening of Cr2Nb Precipitates in Cu-8 Cr-4 Nb Alloy

High Temperature Coarsening of Cr2Nb Precipitates in Cu-8 Cr-4 Nb Alloy

National Aeronautics and Space Admini
Anderson, Kenneth Reed

Hardcover

Technology & EngineeringPhysics

ISBN10: 1025152948
ISBN13: 9781025152943
Publisher: Hutson Street Press
Published: May 22 2025
Pages: 70
Weight: 0.61
Height: 0.25 Width: 6.14 Depth: 9.21
Language: English

A new high-temperature-strength, high-conductivity Cu-Cr-Nb alloy with a CrNb ratio of 2:1 was developed to achieve improved performance and durability. The Cu-8 Cr4 Nb alloy studied has demonstrated remarkable thermal and microstructural stability after long exposures at temperatures up to 0.98 T(sub m). This stability was mainly attributed to the slow coarsening kinetics of the Cr2Nb precipitates present in the alloy. At all temperatures, the microstructure consists of a bimodal and sometimes trimodal distribution of strengthening Cr2Nb precipitates, depending on precipitation condition, i.e. from liquid or solid solution, and cooling rates. These precipitates remain in the same size range, i.e. large precipitates of approximately I pm, and small precipitates less dm 300 nm, and effectively pin the grain boundaries thus retaining a fine grain size of 2.7 micro-m after 100 h at 1323 K. (A relatively small number of Cr-rich and Nb-rich particles were also present.) This grain boundary pinning and sluggish coarsening of Cr2Nb particles explain the retention of good mechanical properties after prolonged holding at very high temperatures, e.g., 75% of the original hardness after aging for 100 h at 1273 K. Application of LSW-based coarsening models indicated that the coarsening kinetics of the large precipitates are most likely governed by grain boundary diffsion and, to a lesser extent, volume diffusion mechanisms.